Heat Shrink end caps are manufactured from a polyolefin material and coated with a hot melt adhesive on the inner surface. This provides a water tight seal against the damage of moisture, dirt or corrosion. The rugged wall of these end caps also offers excellent resistance against abrasion. Suitable for use on polymeric and paper insulated, lead jacketed cables.
Key Features
Shrink ratio of 2:1.
Tensile strength after heat ageing: 168 hours at 120°C - 10 MPa min.
Operating temperaure -55°C to +100°C.
Specification
Material:
2:1 Shrink Ratio, Cross Linked Polyolefin.
Standard Colours:
Black
Operating Temperature:
-55°C to +100°C
Shrink Temperature:
120°C
Longitudinal Change:
+5% to 10%
Dielectric Strength:
20 kV/mm Min.
Thermal Heat Aging:
168 Hours at 150°C, 4 Hours at 200°C; Low Temperature Flexibility 4 Hours at -30°C
Performance:
Will provide a seal at up to 0.05MPa internal pressure whilst operating between -30°C to +70°C.